Igwe anaghị agba nchara akwụkwọ ntuziaka electrode E312-16 weld imepụta
Ngwa
Ọ dị mma maka ụdị ihe nchara ọ bụla siri ike ịgbawa ma dị mfe ịgbawa ma ọ bụ dị mfe ime pores, hardening alloy steel na ihe ndị ọzọ.Na elu carbon ígwè, ngwá ọrụ ígwè na dissimilar ígwè metal ịgbado ọkụ.
Ọkọlọtọ anyị zutere: GB/T983 E312-16, AWS A5.4 E312-16 & A5.4M E312-16, ISO3581-A: E(29 9) R 1 2, ISO3581-B: ES312-16
Òtù asambodo: CE
Ngwakọta kemịkal:
ALOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | |
GB/T iwu | 0.15 | 0.5-2.5 | 1.00 | 28.0-32.0 | 8.0-10.5 | 0.75 | 0.04 | 0.03 | 0.75 | |
Iwu AWS | 0.15 | 0.5-2.5 | 1.00 | 28.0-32.0 | 8.0-10.5 | 0.75 | 0.04 | 0.03 | 0.75 | |
URU Ọmụmaatụ | 0.05 | 1.2 | 0.6 | 28.5 | 8.5 | 0.01 | 0.02 | 0,003 | 0.01 |
ALA nke igwe:
ALA | IKE (MPa) | IKE EXTENSION (MPa) | IMAPACT URU J/℃ | ELONGATION(%) | ||||
GB/T iwu | - | 660 | - | 15 | ||||
Iwu AWS | - | 660 | - | 22 | ||||
URU Ọmụmaatụ | - | 740 | - | 24 |
NDỊ AKWỤKWỌ NDỊ AKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWASỊAKWỤKWỌRỤRỤ
Nkọwapụta DIAMETERS(mm) | 1.2 | 1.6 | ||||||
Volt | 22-36 | 26-38 | ||||||
Amp | 120-260 | 200-300 | ||||||
Ogologo ndọtị akọrọ (mm) | 15-20 | 18-25 | ||||||
Orufe gas (l/min) | 15-25 | 15-25 |
Titanium calcium igwe anaghị agba nchara nwere electrode aka, weld maka usoro austenite-ferrite biphase, ihe mejupụtara ya bụ 29% CR-9% Ni, nke a na-akpọkarị: electrode eluigwe na ala.
Arc kwụsiri ike, nhazi mara mma, ọmarịcha mma, obere splashes, mwepu dị mfe, ezigbo ọkụ na-eguzogide akpụkpọ ọgwụ, ezigbo mgbochi stomatal.
Njirimara igwe kwụsiri ike, ọnụego ngafe X-ray dị elu.
Ningbo Honest Metal Materials Co, Ltd. bụ mba ịgbado ọkụ ọkachamara ụlọ ọrụ n'imedependent nnyocha na mmepe, mmepụta, ahịa na njikwa.E hiwere ya na 2020.
400,000 ton super nnukwu ore ebu
Ngwa ike ọkụ
Ụlọ ọrụ Zhangjiagang Hanzhong Cryogenic Technology Co., Ltd.Ihe nchekwa nke cryogenic
Ngwakọta kemịkal:
ALOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T iwu | 0.15 | 0.5-2.5 | 1.00 | 28.0-32.0 | 8.0-10.5 | 0.75 | 0.04 | 0.03 | 0.75 |
Iwu AWS | 0.15 | 0.5-2.5 | 1.00 | 28.0-32.0 | 8.0-10.5 | 0.75 | 0.04 | 0.03 | 0.75 |
URU Ọmụmaatụ | 0.065 | 1.45 | 0.75 | 29.2 | 9.5 | 0.02 | 0.029 | 0.008 | 0.10 |
ALA nke igwe:
ALA | IKE (MPa) | IKE EXTENSION (MPa) | Okpomọkụ ℃xh | IMAPACT URU J/℃ | ELONGATION(%) | |||||
GB/T iwu | - | 660 | - | - | 15 | |||||
Iwu AWS | - | 660 | - | - | 22 | |||||
URU Ọmụmaatụ | - | 805 | - | - | 24 |
NDỊ AKWỤKWỌ NDỊ AKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWASỊAKWỤKWỌRỤRỤ
Nkọwapụta DIAMETERS(mm) | 2.0 * 250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
ELECTRICITY (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 |