Akwụkwọ ntuziaka igwe anaghị agba nchara Electrode E316L-17 nnukwu mmiri na-ebu gas weld
Teknụzụ ịgbado ọkụ
Ekwela ka ajụjụ ndị ahụ
Gaa n'ihu na-akpagbu gị
Arc enweghị ntụkwasị obi
Ịkpụzi na-adịghị mma
Ọfụfụ dị ukwuu
A na-ejikarị fatịlaịza, urea, petrochemical
mmepụta ma ọ bụ nchekwa akụrụngwa dị mkpa Ọdịdị
Pot acid ụdị igwe anaghị agba nchara electrode aka, jet arc, isi
Akụrụngwa dị obere C-18%Cr-12%Ni-2%Mo, ezigbo ihe mgbochi corrosion.
Ripple dị mma
Ọmarịcha ịgbado ọkụ ọrụ, mgbape eguzogide, porosity eguzogide bụ magburu onwe ya
Ihe mkpuchi ahụ nwere ezigbo nguzogide ọkụ, ihe nrụpụta igwe kwụsiri ike nke igwe ejikọtara ọnụ yana oke iru eru X-Rav
Mfe slagging
Usoro ngwaahịa
Ngwakọta kemịkal:
ALOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Ndị ọzọ |
GB/T iwu | 0.029 | 0.61 | 0.78 | 0.029 | 0,006 | 11.58 | 18.4 | 2.5 | 0.07 | - |
ALA nke igwe:
ALA | IKE (MPa) | IKE EXTENSION (MPa) | IMAPACT URU J/℃ | Ọgwụgwọ okpomọkụ °C*h | ||||
GB/T iwu | 580 | 38 | - | - |
NDỊ AKWỤKWỌ NDỊ AKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWASỊAKWỤKWỌRỤRỤ
Nkọwapụta DIAMETERS(mm) | 2.0 * 250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
ELECTRICITY (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
Nkwado ụlọ ọrụ
Ngwaahịa kwesịrị ekwesị maka a
ọtụtụ ngwa ngwa
Teknụzụ ịgbado ọkụ
85000 m3 buru ibu
Ethane Vinyl Carrier (VLEC)
-
Guangxi Huayi
methanol dehydrating tower
-
Shaanxi Pucheng -50 ℃
propane Spherical tank oru ngo
Ngwakọta kemịkal:
ALOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Ndị ọzọ |
GB/T iwu | 0.029 | 0.61 | 0.78 | 0.029 | 0,006 | 11.58 | 18.4 | 2.5 | 0.07 | - |
ALA nke igwe:
ALA | IKE (MPa) | IKE EXTENSION (MPa) | IMAPACT URU J/℃ | Ọgwụgwọ okpomọkụ °C*h | ||||
GB/T iwu | 580 | 38 | - | - |
NDỊ AKWỤKWỌ NDỊ AKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWỤKWASỊAKWỤKWỌRỤRỤ
Nkọwapụta DIAMETERS(mm) | 2.0 * 250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
ELECTRICITY (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |